Radcolube® 17111 (MIL-DTL-17111) is for use in the hydraulic transmission of power, particularly in naval ordnance hydraulic equipment. This lubricant is blended with greatly advanced mineral base oils and uses additive technology to offer defense against rust and wear. Radcolube 17111 greatly expands viscosity temperature characteristics while offering heightened oxidation and corrosion resistance.
NATO Code
H-575
ISO 9001: 2015 Certification Number
C2021-00038
Military Symbol
MIL-DTL-17111E(1)
National Stock Numbers Available From Radco
9150-00-261-8317 5-Gallon Pails
9150-00-261-8318 55-Gallon Drums
| FINISHED FLUID CHARACTERISTICS | REQUIREMENT | Typical Results | TEST METHOD |
| API Gravity at 15.6°C | Report | 30.7 | ASTM D287 |
| Viscosity at -35°C, max | 1,000 mm2/s (cSt) | 888.8 | ASTM D445 |
| Viscosity at -20°C, max | 500 mm2/s | 287.8 | ASTM D445 |
| Viscosity at +40°C, min | 25 mm2/s | 26.56 | ASTM D445 |
| Viscosity at +100°C, min | 8 mm2/s | 13.11 | ASTM D445 |
| Pour point, max | -40°C | -63 | ASTM D97 |
| Flash point, Cleveland Open Cup, min | 104°C | 104 | ASTM D92 |
| Fire point, Cleveland Open Cup, min | 113°C | 114 | ASTM D92 |
| Neutralization number, max | 0.3 mg KOH/g | 0.12 | ASTM D974 |
| Precipitation number, max | 0.05 ml | 0.001 | ASTM D91 |
| Water | 0.0% | 0.0% | ASTM D95 |
| Color, ASTM D1500, max | 2 | 0.5 | ASTM D1500 |
| Low temperature turbidity, 72 hours at -37°C | ¶ 3.2.4.1 | Conforms | ¶4.5.2.2 |
| Rust prevention | No evidence of rust | PASS | ¶ 4.5.2.3 |
| Corrosion and oxidation stability, 336 hours at 93°C
Copper, weight change, max There shall be no pitting, etching, or visible signs of corrosion Appearance of copper Viscosity at 99°C, percent change Viscosity at -18°C, percent change Neutralization number change, max Insoluble material, percent weight, max Color, ASTM D1500, max |
0.2 mg/cm2
Conform Report 0 to 25% 0 to 25% 0.5 0.5% 5.0 |
+0.001
Conforms 1b +9.71% +23.95% 0.14 0.15% 1.5 |
¶ 4.5.2.4.1 |
| Corrosion and oxidation stability, 72 hours at 93°C
Viscosity at 99°C, percent change Viscosity at -18°C, percent change Neutralization number change of fluid layer, max Acidity of water layer, max |
0 to 15%
0 to 15% 0.5 0.5 mg KOH/g |
+3.58%
+8.49% 0.13 0.05 |
¶ 4.5.2.4.2 |
| Shear stability
Viscosity change at 38°C, viscosity change max. Neutralization number change, max |
-20%
0.2 |
-8.40%
+0.02 |
ASTM D5621 |
| Steel-on-steel wear, max | 1 mm | 0.54 | ASTM D2266 |
| Evaporation, 6 hours at 66°C, max | 20% | 10.25% | ASTM D972 |
| Water sludging, viscosity change at 38°C, max. | -2% to 10% | -0.82% | ¶ 4.5.2.5 |
| Workmanship | ¶ 3.2.5 | Conforms | Visual |